Solvent-induced changes in dimensionality of praseodymium coordination polymers with diphenylphosphorylvalerate ligand

• Autoři: SPÍCHAL Zdeněk; PINKAS Jiří; NEČAS Marek
• Rok publikování: 2012
• Druh: Článek v odborném periodiku
• Časopis / Zdroj: Polyhedron
• Fakulta / Pracoviště MU: Středoevropský technologický institut
• www: http://dx.doi.org/10.1016/j.poly.2012.08.056
• Doi: http://dx.doi.org/10.1016/j.poly.2012.08.056
• Obor: Anorganická chemie
• Klíčová slova: Diphenylphosphorylvaleric acid; Praseodymium; Coordination polymers; X-ray crystallography
• Popis: Architectures of coordination polymers resulting from the reaction of diphenylphosphorylvaleric acid (1) with Pr(NO3)3.6H2O in the presence of a base can be controlled by the solvent. While in methanolic solution a two-dimensional network Pr2(1–H)3(NO3)3 (1m) with a 1:1.5 metal-to-ligand ratio was formed, the aqueous media induced the formation of a three-dimensional framework Pr(1–H)2(NO3) (1w) with a 1:2 metal-to-ligand ratio. The compounds were studied by single crystal X-ray diffraction, IR spectroscopy, ESI-TOF mass spectrometry, and thermal analysis TG/DSC techniques.

Související projekty

• Syntéza a vlastnosti anorganicko-organických polymerních materiálů
• Oxidy a fosforečnany kovů jako formy jaderného odpadu: studium sonochemického srážení, tepelných přeměn a rozpustnosti
• CEITEC - středoevropský technologický institut