Mo-B-C and Ta-B-C Nanostructured Layers with Promising Fracture Toughness

Logo poskytovatele

Varování

Publikace nespadá pod Filozofickou fakultu, ale pod Přírodovědeckou fakultu. Oficiální stránka publikace je na webu muni.cz.
Autoři

BURŠÍK Jiří KUBĚNA Ivo BURŠÍKOVÁ Vilma SOUČEK Pavel ZÁBRANSKÝ Lukáš VAŠINA Petr

Rok publikování 2016
Druh Článek ve sborníku
Konference Defect and Diffusion Forum
Fakulta / Pracoviště MU

Přírodovědecká fakulta

Citace
Doi http://dx.doi.org/10.4028/www.scientific.net/DDF.368.107
Obor Fyzika plazmatu a výboje v plynech
Klíčová slova nanolaminate; FIB; SEM; TEM; fracture toughness
Popis X-B-C (X=Mo, Ta) layers prepared by magnetron sputtering were tested. Mechanical properties were characterized by means of nanoindentation experiments in both the static and the dynamic loading regime. The results were correlated with observations of the microstructure under indentation prints by means of scanning and transmission electron microscopy on cross sections prepared using a focussed ion beam. An excellent fracture resistance of prepared nanostructured coatings was found.