Synthesis and characterization of WS2/SiO2 microfibers

Varování

Publikace nespadá pod Filozofickou fakultu, ale pod Přírodovědeckou fakultu. Oficiální stránka publikace je na webu muni.cz.
Autoři

KUNDRÁT Vojtěch ROSENTSVEIG Rita BRONTVEIN Olga TENNE Reshef PINKAS Jiří

Rok publikování 2021
Druh Článek v odborném periodiku
Časopis / Zdroj Journal of Materials Science
Fakulta / Pracoviště MU

Přírodovědecká fakulta

Citace
www https://link.springer.com/article/10.1007%2Fs10853-021-05979-y
Doi http://dx.doi.org/10.1007/s10853-021-05979-y
Klíčová slova Electrospinning; Tungsten disulfide; Silicotungstic Acid; Polyvinyl alcohol; Fibers
Popis Tungsten disulfide polycrystalline microfibers were successfully synthesized by a process involving electrospinning, calcination, and sulfidation steps. We used an aqueous solution of silicotungstic acid (H4SiW12O40) and polyvinyl alcohol as precursors for the synthesis of composite fibers by the needle-less electrospinning technique. The obtained green composite fibers (av. diam. 460 nm) were converted by calcination in air to tungsten oxide WO3 fibers with traces of SiO2 and a smaller diameter (av. diam. 335 nm). The heat treatment of the WO3 fibers under flowing H2/H2S/N2 stream led to conversion to tungsten disulfide WS2 with retention of the fibrous morphology (av. diam. 196 nm). Characterization of the intermediate and final fibers was performed by the XRD, SEM, TEM, HAADF STEM EDS, elemental analyses ICP-OES, and IR spectroscopy methods.