Structure Changes in Superaustenitis Steel During Long-Term Annealing

Logo poskytovatele

Varování

Publikace nespadá pod Filozofickou fakultu, ale pod Fakultu informatiky. Oficiální stránka publikace je na webu muni.cz.
Autoři

SVOBODA Milan SOPOUŠEK Jiří VŘEŠŤÁL Jan

Rok publikování 2002
Druh Článek ve sborníku
Konference Procedings of the VIII Seminar Diffusion and Themodynamics of Materials
Fakulta / Pracoviště MU

Fakulta informatiky

Citace
Obor Fyzikální chemie a teoretická chemie
Klíčová slova ThernoCalc;phase;equilibrium
Popis From the poinnt of view of technology, the long-tem annealing, connected with diffusion of substitutional elements and corresponding structure development, is very important, because it influences the longevity of materials in exploitation conditions. Therefore, the structural study was performed on austenitic anticorrosion steels Avesta 254 SMO and Nicrofer 3033 after annealing 700stC/3188 hrs. Camparision was made with previous results obtained after annealing 700stC/500hrs. Structure development is compared with calculated phase diagram.