Synthesis and characterization of Cu/Ag alloy nanoparticles

Investor logo
Investor logo

Warning

This publication doesn't include Faculty of Arts. It includes Central European Institute of Technology. Official publication website can be found on muni.cz.
Authors

VYKOUKAL Vít VŘEŠŤÁL Jan BURŠÍK Jiří SOPOUŠEK Jiří ZOBAČ Ondřej PINKAS Jiří

Year of publication 2014
Type Conference abstract
MU Faculty or unit

Central European Institute of Technology

Citation
Description Nanoparticles of Cu/Ag alloy were prepared by solvothermal synthesis from different metal precursors. A mixture of metal precursors was dissolved in small amount of oleylamine and injected into mixture of octadecene and oleylamine at 230 °C. Oleylamine acted as a reducing agent and protecting layer on the surface of arising nanoparticles. After 10 minutes reaction mixture was cooled, centrifuged and three times washed with hexane. Obtained nanoparticles were dispersed in hexane. The colloidal solutions of nanoparticles were characterized by dynamic light scattering (DLS), small angle X-ray scattering (SAXS), ultraviolet-visible spectroscopy (UV-VIS). Isolated nanopowders were characterized by transmission and scanning electron microscopy (TEM, SEM) and powder X-ray diffraction (PXRD). Alloy phase transformations were studied by differential scanning calorimetry (DSC). Surface of nanoparticles was characterized by infrared spectroscopy (IR) and mass spectrometry (MS) The results of thermal analysis were compared with the calculated phase diagram. Acknowledgement: Financial support of the COST LD 11046, CEITEC-MU CZ.1.05/1.1.00/02.0068, and GACR 108/14-12653S are gratefully acknowledged. Authors thank Dr. T. Klumpler (Single Crystal X-ray Diffraction Core Facility CEITEC) for the SAXS measurements.
Related projects:

You are running an old browser version. We recommend updating your browser to its latest version.