Phase Diagram in Iron-rich Corner of the Fe-Cr-Mo-V-C System below 1000 K

Logo poskytovatele
Logo poskytovatele

Varování

Publikace nespadá pod Filozofickou fakultu, ale pod Fakultu informatiky. Oficiální stránka publikace je na webu muni.cz.
Autoři

KROUPA Aleš COUFALOVÁ Martina HAVRÁNKOVÁ Jitka COUFALOVÁ Martina SVOBODA Milan VŘEŠŤÁL Jan

Rok publikování 2001
Druh Článek v odborném periodiku
Časopis / Zdroj Journal of Phase Equilibria
Fakulta / Pracoviště MU

Fakulta informatiky

Citace
Obor Termodynamika
Klíčová slova Thermodynamics; Phase Diagrams; Iron; Chromium; Molybdenum; Vanadium; Carbon
Popis Relevant experimental phase equilibria were used with the THERMOCALC program to refine thermodynamic parameters for low-temperature region, in the steels with composition 0.4 to 2.5 wt.% Cr, 0 to 1 wt.% Mo, and 0 to 0.5 wt.% V. The refined parameters were used to calculate phase relationships, which were then compared with experimental results. Results of experiments indicate that M7C3 replaces M23C6 carbides in the temperature region betweeen 773 and 873 K. Similar behavior was also found for molybdenum-rich phases M6C and M2C. Some modifications of existing thermodynamic parameters in the low temperature region were necessary.